2.4665 Hastelloy X ASTM B435

1.Type: Plate, Sheet, Strip, Coil
2.Length: 0-12m
3.Width: 0-2500mm
4.Thickness: 0.3-1200mm
5.Process: Hot/Cold Rolled
6.Surface: 1,2D,2B BA,3,4,6,7

Send Inquiry

Product Introduction

2.4665 Hastelloy X is a high temperature alloy consisting of a nickel-based material with added elements such as chromium, iron and molybdenum, known for its excellent oxidation resistance and high temperature strength. ASME SB 435 UNS N06002 maintains extremely high strength and stability at high temperatures, up to 1200°C. Alloy X has strong corrosion resistance, especially in sulfur-containing atmospheres and oxidizing environments. Hastelloy X is a material widely used in aerospace, chemical processing and industrial heating systems.

ASTM B435 Hastelloy X Plate Application:

Aerospace
Chambers, Turbine Blades
Chemical processing
reaction vessels, heat exchangers
Industrial heating systems
Industrial boilers and heat exchangers

ASTM B435 UNS N06002 Plate Sheet Strip Specification

Specification	ASTM B435 / ASME SB435
Thickness	Ranging from 0.3mm to 20mm
Length	2000 mm / 2440 mm / 2500 mm / 3000 mm / 6000 mm.
Width	1000mm / 1219mm /1250mm / 1500mm / 2000mm
Hardness	As per ASME A & NACE MR 175
Finish	Hot rolled plate (HR), Cold rolled sheet (CR)

EN 2.4665 Hastelloy X Plate Material Composition:

Nickel (Ni): 47.0-50.0%
Chromium (Cr): 20.5-23.0%
Iron (Fe): 17.0-20.0%
Molybdenum (Mo): 8.0-10.0%
Cobalt (Co): 0.5-2.5%
Titanium (Ti): 0.15% (max)
Manganese (Mn): 1.0% (max)
Silicon (Si): 1.0% (max)
Aluminum (Al): 0.50% (max)
Carbon (C): 0.10% (max)
Phosphorus (P): 0.04% (max)
Sulfur (S): 0.03% (max)

ASTM B435 standard:

ASTM B435 / ASME SB 435 is an international standard for nickel alloy plates, strips and sheets. The standard specifies the chemical composition, mechanical properties and dimensional tolerances of the material to ensure the quality and consistency of the alloy products. Hastelloy X is produced and tested in accordance with the ASTM B435 standard to ensure its reliability in various applications.