2.4375 Nickel Alloy K500 Pipe

1. Standard: ASTM B165, ASTM B163, ASTM B725, ASTM B829
2. Size: 6.35 mm OD up to 254 mm OD
3. Thickness: SCH5~SCHXXS
4. Equivalent: UNS N05500, WNR.2.4375, Monel K500

Send Inquiry

Product Introduction

2.4375 Nickel Alloy K500 Pipe has enhanced mechanical properties due to the addition of aluminum and titanium, which gives the alloy precipitation hardening characteristics. Excellent resistance to a variety of corrosive environments, including seawater, acidic and alkaline media. N05500 material maintains non-magnetic properties even at low temperatures. Mechanical properties are maintained over a wide temperature range from sub-zero to high temperatures. We are an Monel K500 supplier with 15+ export experience, contact us for more information and free quotes!

Nickel Alloy K500 Pipe Tube Applications:

Marine Engineering
Chemical Processing
Oil and Gas
Aerospace
Electronic Components

Monel K500 UNS N05500 Nickel Alloy Tube Specification

Specifications	ASTM B 163 ASME SB 163 / ASTM B 165 ASME SB 165
Dimensions	ASTM, ASME and API
Size	15″NB TO 150″NB IN
Specialized in	Large Diameter Size
Range	6.35 mm OD upto 254 mm OD in 0.6 TO 20 mm thickness.
Type	Seamless / ERW / EFW / Welded / EFW / Fabricated
Form	Round, Hydraulic Etc
Length	Single Random, Double Random & Cut Length.
End	Plain End, Beveled End, Treaded
Dimensional	ANSI/ ASME B36.10, B36.19

Monel K500 Round Pipe Chemical Material Composition

Ni	63.0 min
C	0.25 max
Al	2.3 – 3.15
Mn	1.5 max
Si	0.5 max
Fe	05 – 2
Cu	27.0 – 33.0
S	0.010 max
Ti	0.35 – 0.85
Cr	–

Mechanical Properties of 2.4375 Nickel Alloy K500 Tubes

Density	8.44 g/cm3
Melting Point	1350 °C (2460 °F)
Yield Strength (0.2%Offset)	Psi – 1,15,000 , MPa – 790
Tensile Strength	Psi – 1,60,000 , MPa – 1100
Elongation	20%

Pressure of Monel Alloy K 500 Hollow Pipe

Pipe O.D. (in.)	Wall Thickness of Pipe/Tube (inches)
	0.028	0.035	0.049	0.065	0.083	0.095	0.109	0.120
	Working Pressure (psig)
1/8	7900	10100
1/4	3700	4800	7000	9500
5/16		3700	5400	7300
3/8		3100	4400	6100
1/2		2300	3200	4400
3/4			2200	3000	4000	4600
1				2200	2900	3400	3900	4300

Fabrication and Heat Treatment

Machining Monel K500: Alloy 500 is more difficult to machine than many other materials due to its high strength and tendency to work-harden.
Welding Monel K500: Can be welded using common techniques, though care must be taken to avoid cracking.
Monel K500 Heat Treatment: The alloy can be precipitation hardened (age-hardened) to enhance its mechanical properties. This involves heating to a specific temperature and then cooling under controlled conditions.