Alloy 800 Tube

1. Equivalent: UNS N08800, din 1.4876, Incoloy 800
2. Diameters: 4.0 - 1219.2 mm
3. Wall thickness: 0.5 to 20mm
4. Service: Cutting, Welding, Fabricated, Customized

Send Inquiry

Product Introduction

Alloy 800 tube, is a nickel-iron-chromium alloy with aluminum and titanium added. ASME SB 163 UNS N08800 is designed for high temperature applications with a service temperature range of approximately 600°C (1112°F) to 1100°C (2012°F), and maintains good performance even at temperatures up to 1100°C. It also has excellent resistance to oxidation, carburization, etc. It can be customized according to the specific needs of customers. Contact us for more information and free quotes!

800 Tube ASTM Material Standard:

ASTM B163: Standard Specification for Seamless Nickel and Nickel Alloy Condenser and Heat-Exchanger Tubes
ASTM B407: Standard Specification for Nickel-Iron-Chromium Alloy Seamless Pipe and Tube
ASTM B515:Standard Specification for Welded Nickel-Iron-Chromium Alloy Tubes
ASTM B514: Standard Specification for Welded Nickel-Iron-Chromium Alloy Pipe

ASTM B407 UNS N08800 tube Mechanical Properties

Temper	800		800H/HT
Tensile Rm	77.8	ksi (min)	65	ksi (min)
Tensile Rm	536	MPa (min)	448	MPa (min)
R.p. 0.2% Yield	22	ksi (min)	25	ksi (min)
R.p. 0.2% Yield	150	MPa (min)	172	MPa (min)
Elongation (2" or 4D gl)	20	% (min)	20	% (min)

Incoloy 800 tube Physical Properties (Room Temperature)

Specific Heat (0-100°C)	460	J.kg-1.°K-1
Thermal Conductivity	11.5	W.m -1.°K-1
Thermal Expansion	14.4	μm/μm/°C
Modulus Elasticity	208	GPa
Electrical Resistivity	9.89	Ohm-cm
Density	7.94	g/cm³